Tariff Concession Order 0943744 (Cth)

TARIFF CONCESSION ORDER

Under Section 269P of the Customs Act 1901, I, David Mulcair, a delegate of the Chief Executive Officer declare that the goods specified in Column 1 of THE TABLE are goods to which the item in Part III of Schedule 4 to the Customs Tariff Act 1995 specified in Column 2 of THE TABLE applies. This Order shall have effect from 19.11.09 and continue in force until revoked under sections 269SC or 269SD of the Act, or the date, if any, specified in Column 2.

THE TABLE

               COLUMN 1

Description of Goods including the
Customs Tariff Classification

COLUMN 2

Schedule 4 Item Number

Last date of effect

7210.69.00 STEEL SHEET, ALUMINIUM SILICON ALLOY COATED, whether or not in
coil, having ALL of the following:
  (a) width 630 mm, 699 mm, 780 mm, 790 mm, 810 mm, 900 mm,
      914 mm, 930 mm, 990 mm, 1 000 mm, 1 025 mm, 1 030 mm,
      1 035 mm, 1 100 mm, 1 120 mm, 1 146 mm, 1 160 mm,  
      1 165 mm, 1 170 mm, 1 200 mm, 1 219 mm, 1 220 mm, 1 250 mm;
  (b) thickness 0.55 mm, 0.60 mm, 0.72 mm, 0.75 mm, 0.80 mm,
      0.90mm, 0.96 mm, 1.00 mm, 1.15 mm, 1.20 mm, 1.50 mm,
      1.55 mm, 1.60 mm, 1.90 mm or 2.00 mm;
  (c) coating consisting of NOT less than 88% aluminium and
      balance silicon;
  (d) coating weight NOT less than 20 gsm and NOT greater than
      90 gsm;
  (e) conforming to EITHER of the following:
        (i) American Society of Testing and Materials 
            Standards A 463, having ANY combination of the
            following:
             (i) coating symbol T1-25 or T1-40;
            (ii) quality CS or FS or DDS or EDDS;
       (ii) Japanese Industrial Standard JIS G 3314, having ANY
            combination of the following:
             (i) coating symbol 40 or 60 or 80;
            (ii) quality SA1C or SA1D or SA1E

For the purposes of this order tolerances allowable on widths
and thicknesses are:
  (a) widths + or - 2 mm;
  (b) thicknesses + or - 0.2 mm


Op. 19.11.09   - TC 0943744 50

This is page 1 of 1 Page of the above Table.

   ..David Mulcair........................

Dated 05 February 2010   Delegate of the Chief Executive Officer